Khoom npe: ABS Resins
CAS: 9003-56-9 Nr
MF: (C8H8)x·(C4H6)y·(C3H3N)z
wb: 633.91
Khoom Specification
|
Melt Flow Rate (220℃/ 10kg) |
21g / 10 feeb |
|
Specific Gravity (23degree) |
1.03 |
|
Molding Shrinkage |
0.4% ~ 0.7% |
|
Tensile zog 3.2mm (50mm / min) |
500kg / cm32 |
|
Tensile Elongation 3.2mm (50mm / min) |
25.0% |
|
Flexural zog 6.4mm (15mm / min) |
700kg / cm32 |
|
Flexural Modulus 6.4 hli (15 hli / min) |
22000kg / cm32 |
|
IZOD Impact zog 6.4mm ib |
23 degree: 23 kg.cm/cm |
|
-30 degree: - |
|
|
Rockwell Hardness(R-Nqe) |
109 |
|
Thaum tshav kub kub Deflection kub6.4mm, ib (Tsis paub18.6 kg, 18) |
87.0 degree |
|
Vicat Softening Kub(1kg) |
95.0 degree |
|
Flammability(1.5 hli) |
HB chav kawm |
|
Qhuav Taw tes |
75.0℃~ 85.0 degree |
|
QhuavSijhawm |
2h ~ 4 hnub |
|
Lub tog raj kheej Kub |
Rov qab: 180.0℃~ 200.0 degree |
|
Nruab nrab: 190.0℃~ 210.0 degree |
|
|
Pem hauv ntej: 200.0℃~ 220.0 degree |
|
|
Nozzle Kub |
200.0℃~ 230.0 degree |
|
Melt Taw tes |
210.0℃~ 240.0 degree |
|
PwmKub |
40.0℃~ 70.0 degree |
|
INjection Siab |
Txhaj Siab: 60.0MPa ~ 100.0MPa |
|
Tuav Siab: 70.0MPa ~ 90.0MPa |
|
|
Rov qab siab: 0.5MPa ~ 1.0MPa |
|
|
Ntsia Hlau Rotate Ceev |
30.0%~60.0% |